High Manganese Steel Plate Samutprakarn Thailand
HIGH MANGANESE 12-13% , WEAR AND IMPACT RESISTANT STEEL PLATE
CHARACTERISTIC
CREUSABRO® M is a, quench annealed, non magnetic, work-hardening steel with an exceptionally high level of wear resistance when subjected to workhardening by shock or high impact pressure in service. The main characteristic is a superior wear resistance: Severe wear on the surface has a work-hardening effect on the austenitic structure of this steel. This, when combined with the level of carbon in accordance with the international standards, leads to an increase in hardness from 200BHN (in as delivered plates) up to an in-service hardness of at least 550 BHN. This workhardening capability renews itself through out in-service life. The under layers not work-hardened maintain an excellent resistance to shock and a very high ductility.
Delivery Condition
Water Quenching min 200 HB
Yield Strength N/mm2 : –
Tensile Strength N/mm2 : 800 – 1,100
RANGE OF APPLICATION
Safes, Prisons, Armoured Cars, Parts in Beater Mills, in Sand Blaster, Breaker and Crusher Parts, Throat Armour, Grab Crane Parts, Generally for heavy pushing, knocking or blowing stress. By means of these types of stress a strengthening will take place, and in consequence of this, the resistance to wear will go up an up enormously. The more this steel is knocked the higher the hardness and the resistance to wear will be.
CONTACT
การสอบถามเกี่ยวกับผลิตภัณฑ์ข้างต้นข้อมูลบริษัท
เหล็กกล้าคาร์บอน / แผ่นเหล็กกันสึก / ใบเลื่อยสายพาน
เราเป็นตัวแทนจำหน่ายเหล็กเครื่องมือ เหล็กแม่พิมพ์ เหล็กใบตัด เหล็กวิศวกรรม เหล็กแผ่นเกรดพิเศษ เช่น เหล็กแผ่น Corten A ซึ่งมีความทนทานต่อการกัดกร่อนในชั้นบรรยากาศ เรามีความเชี่ยวชาญในการตัดโลหะประเภทต่ ...